MECHANICAL PROPERTIES OF A DEVELOPED FOAMED CONCRETE

F MOHAMMAD; P SHAWNIM

doi:10.26682/sjuod.2017.20.1.45

F MOHAMMAD School of Architecture, Design and the Built Environment, Nottingham Trent University
P SHAWNIM School of Architecture, Design and the Built Environment, Nottingham Trent University

DOI: https://doi.org/10.26682/sjuod.2017.20.1.45

Keywords: Compressive strength, Flexural modulus, Flexural strength, Foamed concrete, Metakaolin, Water reducing admixture.

Abstract

This paper investigates the mechanical properties at a fresh and hardened states of a new foamed concrete. The aim is to develop and produce a hydrophobic lightweight foamed concrete with enhanced properties for structural use. Foamed concrete generally is made of ordinary Portland cement (OPC), fine aggregates, foaming agent, admixtures and water. Metakaolin (MK) and water reducing admixture were used with the mix in this study. The physical properties of the mixes in their fresh state, mainly the consistency of the mixes was determined. All the mixes prepared were undergone rheology test at fixed water/cement (w/c) ratio of 50%, testing for flowability and spreadability. Compressive strength testing was carried out on 100 mm cubes and the results revealed that the compressive strength of foamed concrete decreases with a reduction in density. Flexural strength and flexural modulus, which were tested on 100 x 100 x 500 mm prisms, were also found to decrease with the reduction in density. The use of MK improved compressive strength as well as flexural strength development for normal and foamed concrete. Higher improvement was noted for the flexural strength with the use of a higher dosage of MK.

Downloads

Download data is not yet available.

References

 Amran, Y. H. M., Farzadnia, N. and Ali, A.A.A. (2015). ‘Properties and applications of foamed concrete; a review’, Construction and Building Materials, 101, pp. 990–1005.
 Bing, C., Zhen, W. and Ning, L. (2012). ‘Experimental research on properties of high-strength foamed concrete’, Journal of Materials in Civil Engineering, 24(1), pp. 113–118.
 Brady, G. Watts, and M. Jones. (2001). ‘Specification for foamed concrete’, Highways Agency and TRL Application Guide AG, Vol. 39.
 Brooks J. J. and Johari M.M.A. (2001). ‘Effect of metakaolin on creep and shrinkage of concrete’. Cement and Concrete Composites. Volume 23, Issue 6 , pp 495–502.
 BS EN 12390-5:2009, Testing for hardened concrete, Part 5: flexural strength of test specimens.
 BS EN 12390-8:2009, Testing hardened concrete, Part 8: Depth of penetration of water under pressure.
 BS 1881-122:2011, Testing concrete, Part 122: Method for determination of water absorption.
 BS EN 12390-3:2009, Testing for hardened concrete, Part 3: Compressive strength of test specimens.
 BS EN 15304:2010, Determination of the freeze-thaw resistance of autoclaved aerated concrete.
 BS 11277:2009, Determination of particle size distribution, sieving.
 BS 1881-125:2013, Testing concrete. Methods for mixing and sampling fresh concrete in the laboratory.
 Ding J. and Li Z.. (2002). ‘Effects of metakaolin and silica fume on properties of concrete. ACI Mater J 99(4), pp. 393–398
 Gleize P.J.P., Cyr M. and Escadeillas G. (2007). ‘Effects of metakaolin on autogenous shrinkage of cement pastes’. Cement and Concrete Comp 29, pp. 80–87.
 Jones, M. R. and McCarthy, A.. (2005). ‘Preliminary views on the potential of foamed concrete as a structural material’, Magazine of Concrete Research, Vol. 57, no. 1, pp. 21-31.
 Karl, S. and Wörner, J.D. (1994). ‘Foamed concrete-mixing and workability’, in Rrilem proceedings, pp. 217-217. Chapman & hall.
 Kearsley, E.P., (1999). ‘The effect of high volumes of ungraded fly ash on the properties of foamed concrete’ (Doctoral dissertation, University of Leeds).
 Kearsley, E. P. and Wainwright, P. J. (2001). ‘Porosity and permeability of foamed concrete’, Cement and concrete research, 31, pp. 805-812.
 Khatib J.M. and Clay R.M. (2004). ‘Absorption characteristics of metakaolin concrete’. Cement and Concrete Research 34(1): 19–29.
 Mydin, M.A.O. and Wang, Y.C. (2011). ‘Structural performance of lightweight steel-foamed concrete–steel composite walling system under compression’, Thin-Walled Structures, 49(1), pp. 66–76.
 Nambiar, E. K. K. and Ramamurthy, K. (2006). ‘Influence of filler type on the properties of foam concrete’, Cement and Concrete Composites, Vol. 28, no. 5, pp. 475-480.
 Nambiar, E. K. K. and Ramamurthy, K. (2008). ‘Fresh state characteristics of foam concrete’, Journal of Materials in Civil Engineering, Vol. 20, pp. 111.
 Panesar, D.K, (2013). ‘Cellular concrete properties and the effect of synthetic and protein foaming agents’, Construction and Building Materials, 44, pp. 575–584.
 Poon, C.S., Lam, L., Kou, S.C., Wong, Y.L. and Wong, R. (2001). ‘Rate of pozzolanic reaction of metakaolin in high-performance cement pastes’, Cement and Concrete Research, 9(31), pp.1301-1306.
 Pugh, R.J. (1996). ‘Foaming, foam films, antifoaming and defoaming’, Advances in Colloid and Interface Science, 64, pp. 67–142.
 Ramamurthy, K., Nambiar, E.K.K. and Ranjani, I.S.G, (2009). ‘A classification of studies on properties of foam concrete’, Cement and Concrete Composites, 31(6), pp. 388–396.
 Van Dijk, S. (1991). ‘Foam concrete’, Concrete, Vol. 25, No. 5, July/ August, pp. 49-54.